Title: Análise da resistência à compressão do concreto submetido à altas temperaturas
Author(s): Santos, Hugo Fernandes dos
Pereira, Rayllan Tharlley Cardoso
Wegener, Thiago
First Advisor: Lins, Luciana Nascimento
Summary: Tendo em vista as características de incombustibilidade e baixa condutibilidade do concreto esse estudo objetivou avaliar a variação da resistência à compressão do concreto submetido às temperaturas de 300°C, 500°C e 700°C, para diferentes tempos de exposição em forno mufla. Devido a ocorrência de grandes incêndios nas edificações são observadas diversas alterações na composição do concreto, que compromete sua resistência à compressão. As amostras de concreto utilizadas nos ensaios foram divididas em dois grupos, concreto convencional e concreto com adição de fibra de polipropileno, visando um melhor desempenho na sua resistência sobre a ação do fogo. Simulando uma situação real de incêndio, as amostras foram submetidas ao resfriamento brusco, levando em consideração a pior situação de resfriamento, de acordo com a literatura. Os resultados comprovaram que a partir de 500°C ocorre uma perda significativa da resistência à compressão afetando em mais de 50% a sua capacidade inicial, ocorrendo a formação de fissuras superficiais e mudança da coloração interna. Ao analisar todos os grupos de amostras foi verificado que a fibra de polipropileno não influenciou significativamente nos resultados. Foi observado ainda que quanto maior o tempo de exposição e com o aumento da temperatura, maior a perda da resistência à compressão.
Abstract: Considering the characteristics of incombustibility and low conductivity of the concrete, this study aimed to evaluate the variation of the compressive strength of the concrete subjected to the temperatures of 300°C, 500°C and 700°C, for different exposure times in a muffle furnace. Due to the occurrence of large fires in the buildings, several changes are observed in the composition of the concrete, which compromises its resistance to compression. The concrete samples used in the tests were divided into two groups, conventional concrete and concrete with addition of polypropylene fiber, aiming at a better performance in their resistance to the action of fire. Simulating a real fire situation, the samples were subjected to the sudden cooling, taking into account the worst cooling situation, according to the literature. The results show that from 500 ° C a significant loss of compressive strength occurs affecting more than 50% of its initial capacity, resulting in the formation of superficial cracks and change of the internal coloration. When analyzing all groups of samples it was verified that the polypropylene fiber did not significantly influence the results. It was also observed that the longer the exposure time and the higher the temperature, the greater the loss of the compressive strength.
Keywords: Engenharia civil
Resistência
Incêndio
Concreto
CNPq: CNPQ::ENGENHARIAS::ENGENHARIA CIVIL
Language: por
Parents: Brasil
Publisher: Universidade Católica de Brasília
Institution Abbreviation: UCB
Department: Escola de Exatas, Arquitetura e Meio Ambiente
Program: Engenharia Civil (Graduação)
Citation: SANTOS, Hugo Fernandes dos; PEREIRA, Rayllan Tharlley Cardoso; WEGENER, Thiago. Análise da resistência à compressão do concreto submetido à altas temperaturas. 2018. 23 f. Artigo (Graduação em Engenharia Civil) - Universidade Católica de Brasília, Brasília, 2018.
Access Type: Acesso Aberto
URI: https://repositorio.ucb.br:9443/jspui/handle/123456789/11893
Document date: 2018
Appears in Collections:Engenharia Civil (Graduação)

Files in This Item:
File Description SizeFormat 
HugoFernandesDosSantosTCCGraduacao2018.pdfArtigo1.89 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.